Performance characteristics:
Appearance transparent liquid
Viscosity / mPa.s 25 ℃: 800
Density (25 ℃: 1.03
Shaw hardness: 70
Elongation rate (%): 5
Application of temperature / ℃: -30 ~ 120
250w halogen-wide high-pressure mercury lamp irradiation 5 min: placing 2 H after the test.
Glass / Al ≥ 20 MPa (shear strength)
Glass / stainless steel ≥ 25 MPa (shear strength)
Location and curing properties:
Light intensity (w) (in pressure mercury lamp) 40 1000
Positioning time (S) 10 ~ 20 4 ~ 5
Curing time (S) 60 ~ 80 30 ~ 60
|
|
|
|
| specifications︰ | 10ml
20ml
100ml
250ml |
| Advantages︰ | Application:
Glass and metal, special glass coffee table, glass products, Crystal
Handicrafts, household products, lighting and ceramics, such as bonding
1, the bond must be completely clean dry surface, can not have oil or dust, to avoid affecting performance bond
2, bonding, in a modest infusion glue, the bond will face pinched and exclude air bubbles
3, irradiated with ultraviolet light in the positioning around 5-10 seconds clear excess glue, five minutes of complete cure;
Shuiyin Deng within two minutes of high pressure completely cured
4, no contact with the UV light, may at any time, fixed position
5, (UV) radiation wavelength ultraviolet light: 100 nm ~ 420nm
6, the use of products Kaifeng, to be locking caps, and home with a cool dry place and avoid direct sunlight as
Radio, the use of the remaining glue can not rewind the original packaging, so as not to cause pollution.
7, the goods transparent and almost colorless, odor and small, almost no irritation to the skin.
8, the use of temperature: -30 ℃ ~ +150 ℃
9, the use of products Kaifeng, Jinsuo caps to be home with a cool dry place and avoid too much exposure to direct sunlight
10, durability period: 12 months, after which the trial could continue to use the confirmation of qualified |
|
|